Synthesis of quasicrystal phases by mechanical alloying of Ti45+xZr _38-xNi₁₇ (-4≤ x ≤16) powder mixtures, and their hydrogen storage properties

Keyphrases

• Amorphous Phase 50%
• Annealing 50%
• Crystal Phase 100%
• Desorption Rate 50%
• Electrochemical Hydrogenation 50%
• Elemental Powder Mixture 50%
• Heating Rate 50%
• Hydrogen Atom 50%
• Hydrogen Concentration 50%
• Hydrogen Desorption 100%
• Hydrogen Storage Properties 100%
• Icosahedral 50%
• KOH Solution 50%
• Lattice Parameter 50%
• Mechanical Alloying 100%
• Onset Temperature 50%
• Powder Compact 50%
• Powder Mixture 100%
• Quasicrystal Phase 100%
• Quasicrystals 50%
• Quasilattice 100%
• Rate of Increase 50%
• Small Radius 50%
• Subsequent Annealing 50%
• Ti Concentration 50%
• Ti-rich 50%
• Ti2Ni 100%

Engineering

• Amorphous Phase 50%
• Hydrogen Storage 100%
• Hydrogenation 50%
• Lattice Constant 50%
• Lattice Parameter 50%
• Mechanical Alloying 100%
• Onset Temperature 50%
• Powder Compact 50%
• Powder Mixture 100%
• Rate Increase 50%
• Rate of Heating 50%

Material Science

• Annealing 100%
• Crystalline Material 100%
• Desorption 100%
• Hydrogenation 50%
• Lattice Constant 50%
• Mechanical Alloying 100%
• Quasicrystal 100%